98A Hot Melt Adhesive Low Temperature Lamination Solution Hot Melt TPU for Chemical Hot Melt Sheet and Fire Hose Co-Extrusion with Good Initial

98A Hot Melt Adhesive Low Temperature Lamination Solution Hot Melt TPU for Chemical Hot Melt Sheet and Fire Hose Co-Extrusion with Good Initial Strength

Production Process:

Mold: Solvent processing, Injection molding, Extrusion molding, Calender

Drying requirements: Please dry at 90-100℃ for 3-4 hours;

Injection temperature: 190-195 degrees for the first section, 195-200 degrees for the second section, and 195-210 degrees for the third section

Features:

Excellent physical properties,

Good initial strength & solvent solubility,

Fast crystallization,

Low temperature lamination

Technical Datasheet:

Application:

Low temperature chemical sheet, fire hose co-extrusion, ho tmelt adhesive film, fabrics lamination etc,

Dingzhi Polymer provide wide range of raw material, can be widely used in shoe materials, bag materials, sports equipment, medical equipment, the automobile industry, packaging products, wire and cable coating materials, hoses, films, coatings, inks, adhesives, melt spun spandex fibers, artificial leather, bonded clothing, gloves, air blowing products, agricultural greenhouse, air transportation, and national defense industry.

Please contact us for details.

98A hot melt TPU adhesive

low temperature lamination TPU

hot melt TPU for fire hose

98A Hot Melt Adhesive Low Temperature Lamination Solution Hot Melt TPU for Chemical Hot Melt Sheet and Fire Hose Co-Extrusion with Good Initial Images